| 固化前特性 | 项目 | 数值 | 固化后特性 | 项目 | 数值 |
| 外观 | Aside透明液体 | 硬度 | 57shoreD | ||
| Appearamce | Hardness | ||||
| Bside透明液体 | 折射率 | 1.54 | |||
| Refractindex | |||||
| 密度 | Aside1.03 | 透光率(450nm/1mm) | 98% | ||
| Densityg/cm3 | Lighttransmittance | ||||
| Bside1.02 | 拉伸强度MPa | 5.3 | |||
| Tensilestrength | |||||
| 粘度 | Aside60000 | 延伸率% | 23 | ||
| Viscaosity(25℃,mp.s) | Coefficientof | ||||
| extension | |||||
| Bside50000 | 体积膨胀系数 | 210ppm/℃ | |||
| Volumeexpansion | |||||
| coefficient | |||||
| Mixed48000 | 体积电阻率 | >1×1014Ω.cm | |||
| Volumeresistiviy | |||||
| 可操作时间 | 180 | 介电常数 | 3(60Hz) | ||
| Useaveilabetime(25℃,minutes) | Dielectricconstant | ||||
| 使用条件 | 混合比例 | 3:05 | 击穿电压 | 20~25Kv/mm | |
| MixingratioA:B | Punchthroughvoltage | ||||
| 标准固化条件 | 110℃×1h,150℃ | 弹性模量MPa | 50 | ||
| Standardcuringconditions | ×3h | Modulusofealasticity |